TiO2を含有する鉱滓による微細化黒鉛鋳鉄に関する研究（5）
—S-H鋳鉄の1，2の性質について—（補遺）
1956 年 28 巻 12 号 p. 887-889
詳細
1956 年 28 巻 12 号 p. 887-889
Two test bars with six steps were prepared from cupola melt. They were common gray cast iron having normal flaky graphite structure. After fracture test, microstructure examination and hardness measurement were carried out, it was confirmed that mass effect of S-H cast iron is far less than that of common gray cast iron for structure and hardness.