Separation of Fe-bearing and P-bearing Phase from the Steelmaking Slag by Super Gravity

抄録

The Fe-bearing phase and P-bearing phase were successfully separated from a steelmaking slag by the super gravity and the separated efficiency was improved with increasing the separated time. The P-bearing phase precipitating at 1663 K was intercepted by the filter, while most residual melt went through the filter into the lower crucible to form calcium iron and aluminum and solid solution of iron, magnesium and manganese (RO phase) after centrifugal separation. Under the condition of gravity coefficient G=600 g, T=1663 K and t=15 minutes, the mass fraction of P₂O₅ in the P-bearing slag increased from 2.49 wt% before separation to 3.56 wt% and that of Fe_tO in the Fe-bearing slag from 23.99 wt% to 38.67 wt%. The recovery ratio of P₂O₅ and Fe_tO accounted for 82.2% and 68.5%, respectively.