Evaluation of Solidification Cracking Susceptibility for Austenitic Stainless Steel during Laser Trans-Varestraint Test Using Two-dimensional Temperature Measurement
Dan WangKota KadoiKenji ShinozakiMotomichi Yamamoto
著者情報
ジャーナル オープンアクセス 早期公開

論文ID: ISIJINT-2016-302

この記事には本公開記事があります。
詳細
抄録

Laser beam welding at high speeds enhances solidification cracking susceptibility, and brittleness temperature range must be measured under a high cooling rate to quantitatively evaluate the influence of welding speed upon the susceptibility. This work investigated the influence of welding speed upon the solidification cracking susceptibility of type 310S stainless steel using the laser Trans-Varestraint test. A multi-sensor camera based on two-color thermometry measured two-dimensional temperature distribution around the molten pool to obtain the temperature range along different solidification crack directions, and the applicability and accuracy of the two-dimensional temperature distribution technique for measuring temperature range of cracks was investigated. The brittleness temperature range was measured precisely with this method; it was nearly constant around 102°C at welding speeds from 0.2 to 2.0 m/min. The results demonstrated the effect of the welding speed from 0.2 to 2.0 m/min upon the solidification cracking susceptibility was very small.

著者関連情報
© 2016 by The Iron and Steel Institute of Japan
feedback
Top