Quantification of changes in lattice defect density in BCC iron during plastic deformation using electrical resistivity measurements

抄録

Change in lattice defects density in bcc pure iron due to tensile deformation was quantified by using both electrical resistivity measurements and X-ray diffraction (XRD). As bcc pure irons, ultra-low carbon steel (ULCS) and interstitial free (IF) steel are used as the model specimen. Dislocation density evaluated using Williamson Hall method with XRD shows the saturation with the value of around 3.7×10¹⁵ m^-2for ULCS and around 1.4×10¹⁵ m^-2 for IF steel after plastic strain after ~5%. Increase in electrical resistivity was observed with increasing plastic strain. Consequently, increase in vacancy concentration occurs with increasing plastic strain of around 0.3, such as, 2.6×10^-5 for ULCS and 3.4×10^-5 for IF steel. Additionally, the migration of carbon atoms from grain interior to grain boundary via dislocation might occur at the initial stage of plastic deformation in ULCS.