Phase stability and thermal expansion properties of additive manufactured super-invar alloy

Abstract

Super-invar alloy, Fe–32%Ni–5%Co, is widely utilized in precision instruments due to its remarkably low thermal expansion coefficient. Additive manufacturing holds promise for fabricating complex-shaped components with this alloy. This study investigated the phase stability and thermal expansion properties of Super-invar alloy fabricated via Laser Powder Bed Fusion (AM sample), comparing them to those of conventionally cast material (Re-melt sample). Microstructural analysis indicates that the AM sample has a more stable austenitic structure, attributed to minimal micro-segregation. Furthermore, it was observed that the thermal expansion coefficient decreases consistently with higher cooling rates within the temperature range of 400-300 K. As a result, AM sample exhibits lower expansion coefficient and it maintains at lower temperatures.