In situ Synthesis of TiB2 Particulate Locally Reinforced Steel Matrix Composite by the Self-propagating High-temperature Synthesis Reaction of Al-Fe-Ti-B System during Casting
2004 年 44 巻 11 号 p. 1847-1851
詳細
2004 年 44 巻 11 号 p. 1847-1851
In-situ TiB2 particulate locally reinforced steel matrix composites were successfully fabricated by the self-propagating high-temperature synthesis (SHS) reaction of 10Al-20Fe-Ti-B and 40Al-20Fe-Ti-B systems, respectively, in the molten high chromium alloy steel during casting. Microstructure analysis of the composite showed that the interface bonding between the matrix and locally reinforced region is very good and the locally reinforced region consists of three different regions, i.e. the Fe-rich region, the fine dispersion of TiB2 particulates region and the larger TiB2 particulates region. The wear test showed that the wear resistance of the locally reinforced regions of the composites is higher than that of the steel matrix.