Effect of Spark Plasma Sintering on Densification and Mechanical Properties of Silicon Carbide

Abstract

Silicon carbide ceramics which 5 mass% Al₂O₃ and 2 mass% Y₂O₃ were added to were prepared by the spark plasma sintering (SPS) method under the conditions of 30 MPa and 5 min. Mechanical properties at room temperature were eximined. The SPS brought dense silicon carbide ceramics at a sintering temperature of 1800°C, which was about 200°C lower than that of the hot-pressing process. The silicon carbide obtained by SPS had higher strength and fracture toughness than those obtained by hot-pressing. The results suggest that the inside temperature of the sintered bodies during spark plasma sintering was higher than the measured temperature.