2000 Volume 108 Issue 1263 Pages 993-997
Hg-based superconductors, Hg0.8M0.2Ba2Ca2Cu3Oy (Hg (M) 1223; M=Cr, Mo, W, In, Ru and Sn) were prepared using a high pressure technique and their superconducting properties, Tc and Birr, were investigated. Nearly single-phase samples of Hg (M) 1223 (M=Cr, Mo, In and Ru) were obtained by heating at 1000-1100°C for 1-4h under 6GPa. Tc of the substituted samples was lower than 135K. Enhancement in Birr was observed in Hg (Ru) 1223. A possible explanation for this phenomenon was proposed.