Cracking of a High Strength Steel Charged with Hydrogen in Ammonium Thiocyanate Solution
Mariko Nakamura, Hiroyuki Saito, Norihiro Fujimoto, Yasuhiro Higashi, Takashi Sawada
Author information
Keywords: hydrogen embrittlement, hydrogen, ammonium thiocyanate
JOURNAL FREE ACCESS

2012 Volume 61 Issue 4 Pages 158-160

Details
Download PDF (576K)
Download citation RIS

(compatible with EndNote, Reference Manager, ProCite, RefWorks)

BIB TEX

(compatible with BibDesk, LaTeX)

Text
How to download citation
Contact us
Abstract
The hydrogen embrittlement test of steel samples carried out. The loaded samples are immersed in an ammonium thiocyanate solution. Sub-cracks grew in the transverse direction to the loaded stress on the specimen surface. The most quick-growing crack may cause the fracture of specimen.
Content from these authors
© 2012 Japan Society of Corrosion Engineering
Previous article Next article
Favorites & Alerts

Recently viewed articles
Predecessor

CORROSION ENGINEERING DIGEST

CORROSION ENGINEERING DIGEST

CORROSION ENGINEERING

Share this page
feedback
 Top