2022 Volume 71 Issue 10 Pages 284-287
This study investigated the influence of the drying condition of the mortar specimens and the CO2 partial pressure during accelerated carbonation tests on the carbonation. The results show that when the change of the specimen’s mass due to drying was large and the CO2 partial pressure was high, the carbonation progress increased. Following the accelerated carbonation test, hyperbaric-oxygen accelerated corrosion tests were conducted. As a result, the steel embedded in the mortar specimens was corroded when the carbonation depth was almost the same as the mortar cover.