Photoeffect on Corrosion Behavior of SrTiO3-Coated Galvanized Steel
Jianshun HuangTadashi ShinoharaShigeo Tsujikawa
Author information
JOURNALS FREE ACCESS

2000 Volume 49 Issue 10 Pages 625-631

Details
Abstract

The n-type semiconductor SrTiO3 was coated on the hot-dip zinc coated steel (Z18). Different from the sacrificial zinc coating, the coating acted as a stable photo-anode to offer non-sacrificial catholic protection to substrate steel. With ZnO formed on the galvanized steel by anodizing in 0.1M NaOH aqueous solution, a good photoeffect was found. With the sol-gel derived SrTiO3 additionally coated on ZnO, the photoeffect was further improved. The open-circuit potential was maintained less noble even after stopping illumination for the coating with intermediate Fe-doped SrTiO3 layer, SrTiO3/Fe-SrTiO3/ZnO/Z18. Moreover, photodecomposition that appeared for ZnO-coated galvanized steel could be prevented by the SrTiO3 coating. The couples of SrTiO3//Fe (Fe coupled with SrTiO3/Fe-SrTiO3/ZnO/Z18) and Zn//Fe (Fe coupled with Z18) were developed as ACM (atmospheric corrosion monitor) sensors to evaluate the corrosion behavior of galvanized steel with and without SrTiO3 coating in atmosphere. For the SrTiO3//Fe sensor, an anodic output was detected in the dark to show dissolution of Fe electrode, while it changed to cathodic one upon illumination. The cathodic value was larger than that of Zn//Fe sensor under certain conditions of lower amount of deposited sea salt and lower relative humidities, where substrate steel could be protected from rusting with the non-sacrificial coating.

Information related to the author
© Japan Society of Corrosion Engineering
Previous article
feedback
Top