6000系アルミニウム合金の熱間成形能
伊藤 勉石川 真之大塚 正久佐賀 誠菊池 正夫
著者情報
ジャーナル フリー

2005 年 55 巻 1 号 p. 9-14

詳細
抄録
It has recently been clarified in a previous paper that 6XXX aluminum alloys of medium grain size exhibit a characteristic hot ductility behavior above 773 K, in which the elongation to fracture is minimum in medium strain rate range while it maintains high levels between 200% and 340% both in low and high strain rate. In this paper is discussed the relationship between such ductility behavior and rate controlling mechanisms of deformation and fracture at 803 K. The results are summarized as follows: (1) In spite of the fact that both strain rate sensitivity and ductility are high, hot working at low strain rate is not appropriate if not, for example, superimposing back-pressure because cavitation occurs remarkably at the grain boundaries. (2) Hot working at high strain rate is recommended, not only because productivity is high but also because, in spite of m-values as low as 0.2, the elongation up to 200% is obtained without remarkable cavitation.
著者関連情報
© 2005 一般社団法人 軽金属学会
前の記事 次の記事
feedback
Top