抄録
This is a report on the annealing of cold-rolled high-purity Al-Pb alloys. By measuring the breadth of X-ray rocking curve which was diffracted from a poly-crystal, the anther observed the dislocation movement in softening, recovery and recrystallization of Al-Pb alloys. The result was that in case of cold-worked and then annealed metals of Al-Pb alloys the (220) planes rocking curve breadth did not decrease so rapidly as high-purity aluminium. The integral breadth of (222), (422) planes, sometimes registered different movements from other planes.