Abstract
Aluminum wires drawn up to 50.5, 71.8 and 93.0%in reduction of area were annealed at 340°C for 30min and secondarily drawn. Mechanical testing and determination of (111) pole figures were made. The first drawing texture of the wire drawn by 93% in reduction of area which is inferior in mechanical properties to the textures of the wires drawn by 50.5 and 71.8% remains in the recrystallization and secondary drawing textures. The wire heavily drawn at first is restored no longer mechanical properties by annealing and secondary drawing. The first drawing textures in the wires drawn by 50.5 and 71.8% disappears by annealing, and the strength increases with increase in the secondary drawing ratio.