Abstract
The alloying effect of Cobalt (Co) to microstructural parameters and mechanical properties, such as partitioning ratios of alloying elements and creep strength, of Re-bearing Ni-base single crystal superalloys have been investigated. The second generation single crystal superalloys, TMS-82+, Ni-7.8Co-4.9Cr-1.9Mo-8.7W-5.3Al-6.0Ta-2.4Re-0.1Hf, in mass% (8Co) was compared to a Co-free (0Co) and 15 mass% Co (15Co) alloy which had the same chemical composition as TMS-82+ except that Co was changed.
It was shown that the partitioning ratios of alloying elements tend to k(=Xγ/Xγ′)=1, as the content of Co was increased.
Furthermore, it was found that there was suitable content of Co for the creep strength under various temperature-stress conditions.