抄録
The alignment distribution of Nd2Fe14B grains in NdFeB sintered magnet was measured by electron back-scattering diffraction (EBSD). The alignments and the coercive force decrease ratios were calculated using these alignment distributions. These data were compared against the results obtained from magnetization measurements. From EBSD data, it was found that the alignment distributions of magnets used in this experiment were close to a Gaussian distribution. It was also found that there was no difference in the alignment distribution between magnets with Dy and without Dy. The calculated alignments using the alignment distribution functions were close to the values of magnetization measurements. However, it was found that the calculated coercive force decrease ratios were different from the results obtained from magnetization measurement.