Microstructure and Magnetic Properties of Grain Size Controlled Ba Ferrite Using Hot Isostatic Pressing
S. ItoT. NagatakeY. YamaguchiK. Fujimoto
著者情報
ジャーナル オープンアクセス

2014 年 61 巻 S1 号 p. S255-S257

詳細
抄録
The powder compact of Ba ferrite was directly sintered by hot isostatic press (HIP). Using HIP, grain growth was successfully controlled and densification was achieved at low temperature. The Ba ferrite powder prepared by coprecipitation was densified to 99.6% without grain growth by sintering at 1000°C for 1 h under 200 MPa. The average grain size of the Ba ferrite obtained was 0.2 µm, which was comparable to the particle size of starting powder. This Ba ferrite revealed 10.3 kJ/m3 in (BH)max. This (BH)max was increased to 14.1 kJ/m3 by annealing the Ba ferrite at 1000°C for 1 h under atmospheric pressure. The improvement of (BH)max is due to the relaxation of the internal stress induced by HIP sintering.
著者関連情報
© 2014 by Japan Society of Powder and Powder Metallurgy

本論文はCC BY-NC-NDライセンスによって許諾されています.ライセンスの内容を知りたい方は,https://creativecommons.org/licenses/by-nc-nd/4.0/deed.jaでご確認ください.
https://creativecommons.org/licenses/by-nc-nd/4.0/deed.ja
前の記事 次の記事
feedback
Top