放電プラズマ焼結法により焼結・接合したAg層を有するFeSi2熱電変換モジュールの熱電変換特性
鈴木 裕宣藁谷 真也東 之弘髙澤 勇輝安野 拓也
著者情報
ジャーナル フリー

2015 年 62 巻 6 号 p. 313-317

詳細
抄録

To achieve high performance of thermoelectric conversion module, it is important that the contact electric resistance between thermoelectric element and electrode is decreased. The manufacturing method to perform sintering of FeSi2 powder and joining of the sintered body with Ag metal plates at the same time was examined by using SPS(spark plasma sintering) method. The Ag plates were successfully joined to FeSi2 element by this process. In addition, it was able to lower the resistance of thermoelectric conversion module because the contact electric resistance between the FeSi2 element and the Cu electrode was decreased by joining Ag plates. The thermoelectric conversion modules with various element heights were produced by this process, and the performance of the modules was evaluated under several temperature differences. The most suitable thermoelectric module height, 5 mm, was decided by investigating relations of the module height and the performance. The FeSi2 thermoelectric conversion module consisting of 50 pairs of p-n elements was produced using an element with 5 mm height, and the performance was measured. As a result, the maximum electric power of FeSi2 thermoelectric conversion module of 50 pairs was 1.70 W in the condition of heating temperature at 873 K and/or cooling temperature at 293 K.

著者関連情報
© 2015一般社団法人粉体粉末冶金協会
前の記事 次の記事
feedback
Top