WC-Co超硬合金の粒成長に対するTi(C,N)粒子分散の抑制効果
高田 真之松原 秀彰森 吉弘松田 哲志
著者情報
ジャーナル フリー

2018 年 65 巻 2 号 p. 91-98

詳細
抄録

The WC-Co cemented carbides with the addition of Ti(C,N) base particles with different sizes were fabricated by liquid phase sintering and their microstructures were mainly investigated in detail comparing the microstructure of the alloys with VC and Cr3C2 addition. It was found that the WC grain growth was more strongly inhibited with increasing Ti(C,N) content and with decreasing Ti(C,N) particle size. The degree of inhibition by the addition of Ti(C,N) particle with about 0.1 μm size was lower than that of VC addition and was almost same as that of Cr3C2 addition. Considering the results about the relationship between WC grain size and Ti(C,N) particle size and the analysis of Co phase composition, it was seen that the mechanism of grain growth inhibition by the addition of Ti(C,N) particles was the pinning (Zener) effect by the second phase particle, which was different from the mechanism for the addition of VC and Cr3C2 reported previously. The case that one Ti(C,N) particle contacts plural WC grains was often observed, so that the pinning effect was considered to work by many Ti(C,N) particles neighboring one WC grain. The very important result that the pinning effect by Ti(C,N) addition enable to develop the new type of ultra-fine cemented carbide was obtained in this study.

著者関連情報
© 2018 一般社団法人粉体粉末冶金協会
前の記事 次の記事
feedback
Top