3次元造形のための環境調和型複合材料開発
山下 大喜佐藤 知広齋藤 賢一宅間 正則高橋 可昌
著者情報
ジャーナル オープンアクセス

2024 年 71 巻 6 号 p. 197-201

詳細
抄録

In the machine parts industry, manufacturing with 3D printers that use resin materials is attracting attention because of the demand for complex-shaped products and small-lot production. Although this method does not require a mold, many of the resin materials are petroleum-based resins, and environmental problems are a concern. Therefore, in this study, PLA, which has carbon-neutral properties, was used as the main material. In order to suppress heat generation when used as a mechanical part, a compound containing MoS2, known as a solid lubricant, is used. PLA pellets and MoS2 powder were kneaded in a desktop kneader, formed into wire-like filaments, and shaped into tensile test pieces with a 3D printer using a Fused Deposition Modeling (FDM). In the tensile test, as the amount of MoS2 added increases, the contact area of PLA, which is thought to be due to strength, decreases. Therefore, the tensile strength decreased. On the other hand, the shorter the heat-kneading time of the composite material, the more suppressed the thermal deterioration of PLA and the higher the tensile strength. It is presumed that PLA composite materials with high thermal conductivity combined with MoS2 are greatly affected by thermal deterioration due to heating during kneading.

著者関連情報
© 2024 一般社団法人粉体粉末冶金協会

本論文はCC BY-NC-NDライセンスによって許諾されています.ライセンスの内容を知りたい方は,https://creativecommons.org/licenses/by-nc-nd/4.0/deed.jaでご確認ください.
https://creativecommons.org/licenses/by-nc-nd/4.0/deed.ja
次の記事
feedback
Top