Influence of Chromium Content on Microstructure and Magnetic Properties of Fe-Based Nanocrystalline Alloy Powders
Mayu WatanabeTakuma EnomotoHideki IshigamiIsamu Otsuka
著者情報
ジャーナル オープンアクセス

2025 年 72 巻 Supplement 号 p. S203-S209

詳細
抄録

Fe-based nanocrystalline alloy powders Fe77Cu1Nb3Si5.7B13.3-xCrx (x = 0, 0.5, 1.0, 1.5, 2.0 at%) was produced by our own unique technology atomization process “Spinning Water Atomization Process (SWAP)”. The broad peak of amorphous state was retained for up to chromium content 1.5% in above mentioned composition. The increase in coercive force with heat treatment was suppressed with adding chromium content. Additionally, the rate of rise the magnetic flux density due to nanocrystallization from the amorphous state showed a tendency to increase with adding chromium content. The Fe77Cu1Nb3Si5.7B11.8Cr1.5 nanocrystalline powder showed Hc = 46.2 A/m and Bs = 1.34 T. The Fe77Cu1Nb3Si5.7B11.8Cr1.5 powder exhibited approximately 7% increase in magnetic flux density and 24% decrease in core loss at 1 MHz at Bm = 0.02 T compared to a commercial (Fe0.97Cr0.03)76(Si0.5B0.5)22C2 amorphous powder.

著者関連情報
© 2025 by Japan Society of Powder and Powder Metallurgy

本論文はCC BY-NC-NDライセンスによって許諾されています.ライセンスの内容を知りたい方は,https://creativecommons.org/licenses/by-nc-nd/4.0/deed.jaでご確認ください.
https://creativecommons.org/licenses/by-nc-nd/4.0/deed.ja
前の記事 次の記事
feedback
Top