WC-Co超硬合金丸棒の液相移動と変形―焼結体中の冷却時温度勾配の寄与―

抄録

Ground round bars made of WC-20 mass%Co cemented carbides were used to accurately determine the changes in shape. The bars were heated at 1673 K and cooled under different conditions to investigate the changes in Co content and diameter (d) in the longitudinal direction. When the bars were heated in a conventional sintering furnace, rapid cooling increased the Co content and d at both ends, while slow cooling increased those at the center. In the latter case, the amount of change was smaller. When the bar was heated using a tubular furnace and then cooled under 30 K of temperature gradient in the longitudinal direction, the Co content and d on the higher temperature side decreased and those on lower temperature side increased. The relationship between the change in Co content and the change in d could be explained quantitatively by considering the migration of the liquid phase in the temperature range of solid-liquid Co coexistence region. This study revealed that when WC-Co cemented carbides were fabricated using the conventional sintering furnace, an inevitable temperature gradient in the specimen during cooing caused the liquid phase migration and the shape distortion, regardless of the cooling rate.