Hot Isostatic Pressing of SnO₂ Prepared by the Hydrazine Method

抄録

Reactive Snot powders have been prepared by the hydrazine method. Their individual particles tend toward a hexagonal morphology with increasing temperature. Well-densified SnO₂ ceramics (99.8% of theoretical) with an average grain size of 0.9μm have been fabricated by hot isostatic pressing for 2 h at 900°C and 196 MPa. Their Vickers hardness and bending strength are -14.4 GPa and -200 MPa, respectively. They exhibit an electrical conductivity of -5 × 10_-3 S⋅cm^-1 at room temperature.