1964 年 1 巻 3 号 p. 93-100
Thermal conductivities of UO2, UC and UC2 were measured with apparatuses developed by the authors. Main results obtained were as follows:
(1) There was no clear evidence of the increase of thermal conductivity of UO2 in the temperature range between 1, 000 ?? and 1, 600 ??, although the effect of radiation transfer mechanism was thought to play a role from the tendency that the decrease of thermal conductivity did cease around 1, 200 ?? .
(2) Thermal conductivities of sintered UC and UC2 pellet-both 95%T.D.-were measured by axial heat flow method. Thermal conductivity of UC was around 0.05-0.04 cal/sec•cm• ?? At the temperature range between 100°and 400°C, while measured values on UC2 were around 0.016-0.014 in the temperature range between 200 ?? And 400 ?? .