Stress Corrosion Cracking of Zircaloy-2 by Metal Iodides

抄録

Some metal iodides such as of Fe, Al, Zr and Te are known to cause stress corrosion cracking (SCC) of Zircaloy just as iodine itself does. Therefore 15 metal iodides were selected as corrodants, and SCC tests were carried out using the internal gas pressurization method.
The results showed that : (1) only those metal iodides which react thermodynamically with Zr to produce ZrI₄ cause SCC of Zircaloy-2; (2) when SCC occurs, the reaction rate between the iodide and Zr seems to be a main factor in determining the SCC susceptibility ; (3) gaseous ZrI₄ is the most corrosive agent ; and (4) some species of metal iodides, such as PbI, cause SCC of Zircaloy-2 more easily than I₂ vapor.
Scanning electron microscope (SEM) examination and electron probe microanalysis (EPMA) on the fracture surface of failed specimens revealed that ZrI, , formed as the reaction product between the metal iodides and Zr, might induce SCC of Zircaloy-2 rather than the iodides themselves.