2018 Volume 62 Issue 1 Pages 44-49
Purpose: The purposes of the present study were to examine the pressure transmission area and maximum pressure transmission of thermoplastic resin denture base materials under an impact load, and to evaluate the modulus of elasticity and nanohardness of thermoplastic resin denture base.
Methods: Three injection-molded thermoplastic resin denture base materials [polycarbonate (Basis PC), ethylene propylene (Duraflex), and polyamide (Valplast) ] and one conventional heat-polymerized acrylic resin (PMMA, SR Triplex Hot) denture base, all with a mandibular first molar acrylic resin denture tooth set in were evaluated (n = 6). Pressure transmission area and maximum pressure transmission of the specimens under an impact load were observed by using pressure-sensitive sheets. The modulus of elasticity and nanohardness of each denture base (n = 10) were measured on 15×15×15×3 mm3 specimen by using an ultramicroindentation system. The pressure transmission area, modulus of elasticity, and nanohardness data were statistically analyzed with 1-way ANOVA, followed by Tamhane or Tukey HSD post hoc test (a =.05). The maximum pressure transmission data were statistically analyzed with Kruskal–Wallis H test, followed by Mann–Whitney U test (a =.05).
Results: Polymethyl methacrylate showed significantly larger pressure transmission area and higher maximum pressure transmission than the other groups (P <.001). Significant differences were found in modulus of elasticity and nanohardness among the four types of denture bases (P <.001).
Conclusions: Pressure transmission area and maximum pressure transmission varied among the thermoplastic resin denture base materials. Differences in the modulus of elasticity and nanohardness of each type of denture base were demonstrated.
This article cannot obtain the latest cited-by information.