Effects of various functional monomers’ reaction on the surface characteristics and bonding performance of polyetheretherketone
Huei-Yu HuangSheng-Wei FengKuan-Yu ChiangYun-Chen LiTzu-Yu Peng Hiroki Nikawa
Author information
JOURNAL OPEN ACCESS

2023 Volume 68 Issue 2 Pages 319-325

Details
Abstract

Purpose: Polyetheretherketone (PEEK) is a new polymeric material that has received significant attention in dentistry because of its mechanical properties, biocompatibility, and aesthetics. However, the bonding performance of PEEK to other materials is not preferable. This study aimed to analyze the variations in the surface characteristics of PEEK under the chemical action of primers containing different functional monomers or polymers and to evaluate the bonding performance of PEEK and dental cement.

Methods: Disk-shaped PEEK samples were prepared by dental milling, blasting with alumina oxide, and covering with primers containing functional monomers or polymers. The surface characteristics of the samples were analyzed by microscopy and spectroscopy. The shear bond strength (SBS) between PEEK and dental cement, with and without thermocycling, was tested using a universal testing machine. Finally, the data were statistically analyzed and compared.

Results: Functional monomers or polymers were successfully bonded to the surface of PEEK. This treatment significantly improved its hydrophilicity and surface free energy (P < 0.05). The primer containing pentaerythritol triacrylate had the highest SBS without thermocycling (13.89 MPa). Meanwhile, the primers containing urethane dimethacrylate (UDMA) and methyl methacrylate (MMA) (abbreviated as the HC group) showed the highest SBS and lowest reduction (25.51%) after thermocycling. Notably, all the testing groups achieved the ISO10477 standard of 5 MPa. After thermocycling, adhesive failure accounted for the largest proportion of failures in all the groups except the HC group.

Conclusions: The chemical priming treatment can significantly improve the SBS of PEEK and dental cement. Moreover, a primer containing both UDMA and MMA can provide improved bonding for PEEK materials.

Content from these authors
© 2024 Japan Prosthodontic Society

This is an open-access article distributed under the terms of Creative Commons Attribution-NonCommercial License 4.0 (CC BYNC 4.0), which allows users to distribute and copy the material in any format as long as credit is given to the Japan Prosthodontic Society. It should be noted however, that the material cannot be used for commercial purposes.
https://creativecommons.org/licenses/by-nc/4.0/
Previous article Next article
feedback
Top