1977 年 43 巻 6 号 p. 1998-2005
Electron microscopy on slightly vacuum-reduced rutile single crystals with a composition of about TiO1.996 revealed the presence of isolated planar faults with {312} fault plane. The displacement vector R of this fault was determined to be R\simeq1⁄2〈10\bar1〉. Discussion was made on the relation between such planar faults and defect centers observed in EPR experiments performed on the same specimens. The result on the displacement vector supports the interpretation of W-spectrum observed in the EPR experiments.