In this study, CrSi2 ceramics were prepared by hot-pressing. The influence of temperature on the electrical conductivity of CrSi2 sintered body was investigated. The samples were sintered at 1273K to 1373K for 3.6ks in vacuum under a pressure of 40MPa. The relative density of sintered body at 1373K was approximately 99%. The high temperature electrical conductivity measured using a D. C. four-terminal method.