2000 Volume 12 Issue 1-2 Pages 105-106
Oxidation behavior of boron phosphide (B13P2) ceramics under the high-temperature conditions was studied. The powder of B13P2 was baked at 773K to 1273K for 2h, 5h, 25h and 50h. The weight gain of B13P was measured as a function of temperature and time. Thermal gravimetric-differential thermal analysis (TG-DTA) was used to measure the weight changes of B13P2 as a function of annealing temperature. TG-DTA plots indicated that B13P2 began to be oxidized at 1050K. Moreover, every baked B13P2 was analyzed by X-ray diffraction analysis. The result of X-ray diffraction analysis showed that B13P2 changed to be amorphous at 1127K.