Tensile Strength of Carbon/Carbon Composites
Hiroshi HATTATatsuji AOIItaru KAWAHARAYasuo KOGOIchiro SHIOTA
著者情報
ジャーナル フリー

2003 年 46 巻 3 号 p. 290-296

詳細
抄録
In order to identify ruling mechanisms of tensile fracture of Carbon/Carbon composites (C/Cs), tensile tests were carried out for various C/Cs as functions of the density, heat treatment temperature, and interfacial strength between fiber and matrix. Three processing routes of preformed yarn, resin char, and HIP processes were adopted to densify C/Cs. These C/Cs were finally heat-treated at temperatures from 2273K to 3300K. The interfacial strength between fiber and matrix was varied by the selection of processing routes. As a result, two ruling failure mechanisms were identified. At density lower than 1.6g/cm3, the tensile fracture was controlled by stress transfer capability from the matrix to reinforcing fibers. However, at higher density than 1.6g/cm3, tensile strength was primarily governed by the interfacial strength between the matrix and fibers. Thus the latter mechanism is nearly same as ceramic matrix composites.
著者関連情報
© 2003 by The Japan Society of Mechanical Engineers
前の記事 次の記事
feedback
Top