Abstract
This study examined the deformation behavior and fatigue crack initiation of a carbon-steel film under cyclic shear loading. As a result,two relations about fatigue behavior were found. Observation of Crystal direction, two relations about fatigue behavior were found. Observation shows that the slip occurred by shear surface outside. On the other hand,generation of the crack by shear surface inside.