Laser ultrasonic technique (LUT) is applicable for measurement under high temperature condition because of the non-contact and remoteness. In this study, LUT was applied to detection the welding defect such as solidification crack and/or lack of penetration at single bevel groove during Gas Metal Arc (GMA) welding process. Nanosecond pulse laser (1064 nm, 60mJ/pulse 100Hz) was used to generate ultrasonic, and was scanned using a galvanometer mirror. Nd:YAG laser interferometer (532 nm, 1W) was used for detection the surface micro vibration caused by arrival of ultrasonic wave. After acquiring the B-scope, which is composed of multi transmit- and receive-points, the synthetic aperture focusing technique (SAFT) is applied. SAFT image obtained by in-process measurement was evaluated to confirm the presence or absence of welding defect indication. As a result, it was possible to indicate the solidification crack and the lack of penetration in the joint even during the welding process. This result suggests that in-process measurement using LUT is very effective technique for detecting weld defects.