SUS304ワイヤにより強化したPLA樹脂複合フィラメントの機械的特性

-芯線への表面処理の効果-

抄録

The purpose of this study is to investigate the mechanical properties of composite filament which made from polylactic acid resin and SUS304 wire for Fused Deposition Modeling. Both of PLA resin and SUS304 wire were supplied to heated extruder for covering the SUS304 wire with melted PLA. The feed rate of both materials was individually controlled by controlling the number of revolutions of stepper motors. In this study, three types of SUS304 wires were used to investigate the effect of surface roughness of wire on the tensile characteristics of composite filament. The surface of SUS304 wire was modified by chemical etching or mechanical grinding to control the surface roughness. For comparing, two modified wires and as received SUS304 wire were used for following experiments. The tensile characteristics of composite filament was investigated by using universal testing machine. Tensile test results showed that the tensile modulus and strength of composite filament was improved compared that of original PLA filament. The pull-out test of composite filament was also revealed that the apparent interfacial shear strength between PLA and SUS304 wire was improved when the surface roughness of SUS304 wire was high. Moreover, when the surface roughness of SUS304 wire was high, the fracture morphology of composite filament was changed.