2233 流動鉛ビスマス中の鋼材の腐食特性と酸素制御特性
近藤 正聡澤田 直樹高橋 実羽田 晃治吉田 晋
著者情報
会議録・要旨集 フリー

p. 241-242

詳細
抄録
Material corrosion test was carried out for some steels exposed in flowing lead bismuth at the conditions where exposure time, temperature, flow rate, flow velocity, and oxygen potential were 1000h, 550℃, 31/min, 1m/s and 3.7×(10)^<-8>wt%, respectively. After the exposure, the steels were analyzed by SEM/EDX and etc. No trace of erosion was observed. Metal corrosion and oxidation were observed and those effects of Cr, W, and Si on corrosion behavior were investigated. It was found that the contents of Cr and W contributed to the film formation, and Si was effective to reduce the corrosion.