1010 Ti-Ni形状記憶合金鋳造材の冷間圧延による効果(S03-2 形状記憶合金の特性と応用技術(2),21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
詳細
The rolling reduction of a cast shape memory alloy (SMA) plate from self-propagating high temperature synthesis (SHS) ingot was investigated. DSC and Tensile test specimens were cast by lost-wax process from SHS ingot. The heat treatment conditions were 400℃-600℃ for DSC and tensile test. Transformation temperatures were measured by differential scanning calorimetry (DSC). Mechanical properties were measured by a tensile test at several temperatures. The effect of rolling reduction was investigating this study.