抄録
The crack bridging behavior of multi-walled carbon nanotube-reinforced alumina matrix composites has been investigated using a single fiber pullout testing method. Contradictory to the conventional understanding (which have reported that pullout phenomena evidently occurred in the bulk nanotube-reinforced alumina composites), the pullout experiments using an in situ SEM method with a nanomanipulator system demonstrated that strong load transfer was revealed, and no pullout behavior was observed for all 15 MWCNTs. The MWCNTs, rather than puffing out from the alumina matrix broke in the outer-shells and the inner section pulled away, leaving the outer-shells of the fragment in the matrix. This implies that tougher ceramics with MWCNT can be obtained by creating the appropriate interaction between the matrix and MWCNT: not too week but also not too strong to permit an adequate load transfer between the two parts and thus a consequent pulling out without breakage of MWCNT. Our finding suggests important implications for design of tougher ceramic with MWCNTs. The important factor for such tougher ceramics will thus be the use of 'strong' NWCNTs having higher mechanical performance (as well as a good dispersion in the matrix).