抄録
Work hardening character of polycrystalline material is studied by using a discrete dislocation plasticity. Grain boundaries are modeled as barriers. Grain size dependences of yield stress and work hardening factor are investigated for model of different grain size, and the result is compared with that of single crystal model. Dislocation pile-up is observed and it is shown that the work hardening property is more significant in fine grain model.