The following conclusions were obtained as a result of examining the fatigue strength characteristic from observation of fatigue testing and a fracture paying attention to damage to the resin / fiber interface in GFRP based modified PC. 1) The damage mechanism was the same although Young's modulus fell PDMS-PC compared with PC-EP. 2) In fatigue testing, the life difference in a high stress region is based on the difference in a damage mechanism.