OS1012 き裂先端近傍の水素凝集挙動に及ぼす荷重負荷形式の影響
大見 敏仁横堀 壽光布川 肇石川 信行
著者情報
会議録・要旨集 フリー

詳細
抄録
Hydrogen embrittlement of steel was caused due to hydrogen in the material. Fracture surface due to hydrogen embrittlement is expected to concern with the local hydrogen distribution around a crack tip, and this distribution depends on the material property and loading condition. On the other hand, slow stress rate test and fatigue test have been conducted for hydrogen embrittlement test using C(T) or smooth tensile specimen. However, concerning stress induced hydrogen diffusion under local stress field, the hydrogen distribution is different depending on the test method and specimen. In this study, hydrogen distributions around a notch tip under fatigue condition were obtained by numerical analysis for uniaxial tensile test and three point bending test. The effect of test method for hydrogen embrittlement was considered.