高強度鋼の超高サイクル疲労における疲労限

抄録

10¹¹ cycles fatigue tests were conducted on high-strength steel to clarify a new fatigue limit in very high cycle regions. The new fatigue limit had not been confirmed by fatigue tests up to 10¹⁰ cycles, while our previous study suggested that the new fatigue limit was probably confirmed by those up to 10¹¹ cycles. However, the 10¹¹ cycles fatigue testing was challenging since it took 2 months even by using ultrasonic fatigue testing at 20 kHz. In this study, 3 specimens were tested beyond 10¹⁰ cycles. Although a test on a specimen was terminated at around 5 x 10¹⁰ cycles, 2 specimens reached 10¹¹ cycles without failure. In other word, no specimen failed above 10¹⁰ cycles. These results demonstrated the existence of the new fatigue limit. The fractured specimens below 10¹⁰ cycles revealed internal fractures originating from oxidetype inclusions. When the specimens failed in very high cycle regions, clear ODAs (Optically Dark Areas) were observed on the fracture surfaces, while the ODAs were obscure in case of failure in conventional life regions. The runout specimens up to 10¹¹ cycles were forcibly fatigue-fractured at higher stress amplitudes in the conventional life regions. As the result, the ODA was observed on the forcibly fatigue-fractured surface. This meant that small internal cracks existed in the runout specimens since the ODA was a trace of small internal crack growth. Namely, non-propagating cracks were the mechanism of the appearance of the new fatigue limit.