抄録

Anodizing was widely used to prepare porous alumina oxide films structure through the thickness and interpore distance. Porous aluminum anodic oxide films fabricated by anodizing in oxalic acid electrolyte containing organic acid were investigated. By controlling them in phosphoric acid corrosion solution for 45 min, high tensile strength alumina templates were obtained. Compared with the surface coating of mild anodization, the tensile strength could be effectively increased from 20.02 MPa to 24.42 MPa.