Gr.122鋼溶接継手のクリープ強度と損傷の評価
本郷 宏通田淵 正明渡部 隆
著者情報
ジャーナル フリー

2011 年 60 巻 2 号 p. 116-123

詳細
抄録

11Cr-0.4Mo-2W-CuVNb steel (ASME Gr.122) has been used for boiler components in ultra-supercritical (USC) thermal power plants. Creep strength of high Cr steel welds decreases due to the formation of Type-IV creep damage in heat-affected zone (HAZ) during long-term use at high temperatures. In the present paper, the creep strength and microstructures of simulated HAZs and a welded joint of Gr.122 steel were investigated. In order to elucidate the processes of Type-IV creep damage, creep tests using thick welded joint specimens were interrupted at several time steps, and the initiation, evolution and distribution of creep voids were measured. It was found that Type-IV creep voids grew after 0.5 of life and a crack formed after 0.9 of life. Creep damage was observed mostly at 1/3 below the surface of the plate. Differences of the Type-IV damage processes between Gr.91 and Gr.122 steel weld were discussed. Experimental creep damage distributions were compared with computed versions using finite element method and damage mechanics analysis.

著者関連情報
© 2011 日本材料学会
前の記事 次の記事
feedback
Top