リアルサイズのモデル複合材料を用いたモードI繊維/樹脂界面破壊じん性の評価
小岩 康三田中 拓中井 善一伊藤 真也
著者情報
ジャーナル フリー

2012 年 61 巻 2 号 p. 183-188

詳細
抄録

A model composite method was proposed to evaluate the interfacial fracture toughness between fiber and matrix, where the resin fracture is not involved. In the composite, two glass fibers from 10 to 15μm in diameter were bonded by resin. In the present study, two kinds of surface treatments were conducted for the glass fibers. One was the acrylic-silane coupling, and the other one was the 3-methacryloxy-propyl tri-ethoxysilane coupling. The interfacial strength is low for the former and it is high for the latter. Two kinds of resins were also employed for the matrix, one was vinylester resin, and the other one was unsaturated polyester resin. The former is ductile and the latter is brittle. In-situ observation testing system was developed for Mode I fracture toughness tests of the model composite, where the resolution of applied force was about 0.01 mN. For the model composites consisted of either the low interfacial strength fiber and the ductile resin or the high interfacial strength fiber and the brittle resin, the crack propagation was unstable, and the interfacial fracture toughness could be evaluated. On the other hand, ductile fracture occurred in the resin and the interfacial fracture was not evaluated for the model composite consisted of the high interfacial strength fiber and the ductile resin.

著者関連情報
© 2012 日本材料学会
前の記事 次の記事
feedback
Top