αCu-Al単結晶の球状圧子による変形機構
III. 〈211〉方向複数回摩擦の場合
1990 年 39 巻 447 号 p. 1663-1669
詳細
1990 年 39 巻 447 号 p. 1663-1669
In the present study the repeated scratch tests were made on the (111) face of the αCu-Al single crystals in the ‹211› and ‹110› directions with a unidirectional or reciprocating motion. After the (111) face had been scratched, the face was electropolished to remove a thin layer of suitable thickness. The slip systems and the etch pit distributions were observed on the exposed surfaces.
The results obtained are as follows:
(1) The deformations produced by scratch in the [211] direction are found to be more pronounced than those in the [211] scratch. The active slip systems on both sides of the scratched track differ from those observed under the track.
(2) The scratched tracks and the slip traces on the scratched faces and the dislocation distributions inside of the material show that the deformation produced by the unidirectional scratch is more remarkable than that produced by the reciprocating scratchs in both cases of ‹211› and ‹110› directions.