抄録
To establish the measuring technique of neutron diffraction for the internal residual stress distribution in a structural component, a neutron diffraction apparatus was designed and manufactured in Modified Japan Research Reactor 3 (JRR3M). At the first step of measurement, a basic characteristics of the diffractometer was evaluated. The incident neutron beam flux was 104n/cm2/sec and the Full Width at Half Maximum (FWHM) was about 0.3 degree. This indicates that the manufactured neutron diffractometer is capable for the residual stress measurement. As the first application of the neutron diffraction measurement, the residual stress distribution in plastically bent carbon steel plate was measured. A typical compressive-tensile-compressive-tensile residual stress pattern in the tangential directiton in the bent plane was confirmed. The maximum stress near the surface was about 180MPa. This means that the technique far residual stress measurement by neutron diffraction can be established in Japan.