316FR鋼厚板溶接継手における溶接金属および熱影響部のクリープ変形挙動
本郷 宏通山崎 政義渡部 隆衣川 純一田辺 龍彦門馬 義雄中澤 崇徳
著者情報
ジャーナル フリー

1999 年 48 巻 2 号 p. 116-121

詳細
抄録
Using hot-rolled 316FR stainless plate (50mm thick) and 16Cr-8Ni-2Mo filler wire, a narrow-gap welded joint was prepared by GTAW (gas tungsten arc welding) process. In addition to conventional round bar specimens of base metals and weld metal, full-thickness joint specimens were prepared for creep test. Creep tests were conducted at 550°C in order to examine creep deformation and rupture behavior in the weld metal of the welded joint. Creep strain distribution on the surface of the joint specimen was measured by moiré interferometry. In the welded joint, creep strength of the weld metal zone apart from the surface was larger than that in the vicinity of the surface due to repeating heat cycles during welding. Creep strain and creep rate within the HAZ adjacent to the weld metal zone were smaller than those within the base metal zone. Creep rate of the weld metal zone in the welded joint was smaller than that of the weld metal specimen due to the restraint of the hardened HAZ adjacent to the zone. The full-thickness welded joint specimens showed longer lives than weld metal specimens, though the lives of the latter was shorter than those of the base metal (undermatching). In the full-thickness welded joint specimen, crack started from the last pass layer of the weld metal zone and fracture occurred at the zone. From the results mentioned above, in order to evaluate the creep properties of the welded joint correctly, it is necessary to conduct the creep test using the fullthickness welded joint specimen which includes the weakest zones of the weld metal, the front and back sides of the plate.
著者関連情報
© 日本材料学会
前の記事 次の記事
feedback
Top