多孔質フライアッシュの組織制御とゼオライト化による強度変化
2003 年 52 巻 6 号 p. 601-605
詳細
2003 年 52 巻 6 号 p. 601-605
The porous fly-ash ceramics with various porosity were prepared using colloidal process with molten wax. Polyethylene terephthalate powders were used combustible pore-forming agents. The total porosity of porous fly-ash increased with the polyethylene terephthalate powder content. The flexural strength of porous fly-ash drastically decreased as the total porosity increased. By the treatment of the sintered fly-ash with 3mol/dm3 NaOH solution at 383K for 15h, phillipsite, a kind of zeolite, was formed on the sintered fly-ash surface. The flexural strength of sintered fly-ash decreased to half of the original value by the zeolitization treatment.