Thermally Enhanced Glass Formation in Multilayered Cu₃₃Zr₆₇ Composite Particles

抄録

A single phase of glassy Cu₃₃Zr₆₇ powders has been synthesized by post-annealing the mechanically alloyed Cu₃₃Zr₆₇ composite powders at 685 K for 1.8 ks. The heat of glassy phase formation was measured directly and found to be −2.59 kJ/mol. The glassy powders transform to big-cube CuZr₂ metastable phase (E9 structure) upon heating to 760 K. This metastable phase does not withstand against the temperature increasing during the DSC analysis and therefore transforms completely into the most stable phase of tetragonal CuZr₂ (C16 structure) at 918 K.