Microstructure and Magnetic Properties for Highly Coercive FePt Sputtered Films

抄録

In this paper, we review our recent investigations on the magnetic properties and microstructure of highly coercive FePt films prepared on both MgO (001) and MgO (110) substrates with various film thicknesses (t_N). Perpendicularly magnetized FePt (001) film were obtained on MgO (001) substrates, while FePt (101) films with the easy magnetization axis canted from the perpendicular direction to the film plane were obtained on MgO (110) substrates. The film morphology changes from a particulate to a continuous state depending on t_N. A drastic decrease in the coercivity has been observed with the percolation of particles for FePt (001) films, when t_N exceeds a critical thickness, t_c=45 nm. On the other hand, the gradual decrease of H_c with t_N has been observed in FePt (101) films and no remarkable change is seen at the critical thickness where the film morphology changes from a particulate to continuous state.